The quality of steel ball determines the efficiency in the working process. If the quality of the steel ball purchased is not up to the standard, it will cause the steel ball to be easily damaged during the working process. What are the common problems of the wear-resistant steel ball during the operation? In this article, the common problems of the steel ball are introduced in detail. What are the main aspects? 

1、the abrasion is high: the main reason is that the manufacturer has no quenching equipment, the wear resistance of the steel ball without the quenching treatment is very low, or the hardness of the steel ball is low due to the secondary charging, so that the abrasion is high;

2、crushing: the main reason is that the composition of the steel ball is not up to standard, the heat treatment mode is wrong, the appearance is poor, or the use of inferior raw materials, resulting in high internal inclusions of the steel ball, resulting in breakage;

3、peeling: the cause is similar to the cause of breakage;

4、 poor appearance: steel ball appearance of serious slag, sand, pile, wrinkle and other appearance defects, and this. The defect points are the stress concentration points of the steel ball, and the steel ball can be caused by the stress change during the use of the ball mill. Crushing or peeling, etc.